HP2023JN densitas inferior Polyethylene est gradus aptus ad sarcinam generalem destinatam. Melius deprimunt, bonas proprietates opticas et mechanicas exhibent. HP2023JN lapsus et antiblock additamenta continet.
EXEMPLAR APPLICATIONS
Tenues recusant pelliculas, laminationes pelliculas, saccos efficiunt, textilia packaging, bona mollia packaging, sacculus generalis propositi cum bonis perspectivis et t-shirts ferebat saccos.
Properties
POTESTAS
VALUES typicus
UNITS
PROBATIO METHODS
POLYMER POLYMER
O Rate conflandum
ad 190°C et 2.16 kg
2
g/10 min
ASTM D1238
Density
ad 23°C
923
kg/m³
ASTM D1505
FORMULA
lapsus agentis
-
-
Anti obstructionum agente
-
-
MACHINA
Fortitudo telum Impact
2
g/µm
ASTM D1709
OPTICIUS POTESTAS
Obducto (1)
8
%
ASTM D1003
Glossa
ad 45°
61
-
ASTM D2457
MODUM PROPRIETATIS
Distrahentes Properties
accentus confractus, MD
20
MPa
ASTM D882
accentus intermissum, TD
15
MPa
ASTM D882
intendere confractus, MD
300
%
ASTM D882
tendunt ad jugum, TD .
588
%
ASTM D882
accentus at cede, MD
12
MPa
ASTM D882
accentus at cede, TD
12
MPa
ASTM D882
1% modulus secans, MD
235
MPa
ASTM D882
1% modulus secans, TD .
271
MPa
ASTM D882
CONDICIONESQUE
Conditiones processus typicae pro HP2023JN sunt:
Ferocactus temperatus: 160 - 190°C
Ratio conflare: 2.0 - 3.0
SANTE, SALUS ET VICTUS CONTACT AGENDI RATIO
Detailed informationes providetur in materia Safety Datasheet et vel Standard Cibus Declaratio, Additionalcertae informationes peti possunt per officium locale Sales.
DECLAMATOR: Hoc productum non destinatur nec debet adhiberi in applicationibus pharmaceuticis/medicis.
Repono et TRACTATIO
Polyethylenae resina eo modo condi debet, ne directa expositio ad solem et/vel calorem reiciatur. Tabularium etiam arescere debet ac potius 50°C non excedere. SABIC warantizare non daret condiciones repositionis malae quae ad qualitatem depravationis inducere possunt sicut color mutatio, malus odor et inadaequata effectio producti. Suadetur ut PE resinae processus intra 6 menses post partum