leve pondus,facilis processus,superficies optima,insulatio electrica.
Late adhibitus in ludicris, interioribus autocineticis, apparatibus electronicis et electricis, componentibus apparatuum domesticorum, etc.
In sacculo parvo 25kg, 27MT cum pallet
Unitas
Specificatio
Resultatum
Methodus Probationis
Index Fluxus Liquefactionis
ml/10 min
220°C × 10KG
18
1133
Densitas Massae
g/cm³
23°C
1.05
1183
Robur Tensilis
MPa
50 mm/min, proventus
47
527
50 mm/min, fractura
34
Elongatio Tensilis
%
50 min/min
30
Modulus Flexionis
GPa
2 mm/min
2.2
CLXXVIII
Robur Flexurale
Robur Impactus Izod
KJ/m²
23°C Incissus
-30°C Incissus
Temperatura Molliendi Vicat
Celsius
1 kg, 50°C/h
°C
5 kg, 50°C/h
Temperatura Distortionis Caloris